Farbacoat EP-152

Two-component enamel to protect the internal surfaces of pipelines, metal containers, tanks, metal structures from chemical and abrasive impact.

Enamel Farbacoat EP-152 is a two-component enamel that forms a coating that combines the high adhesive and protective properties of epoxy and perchlorovinyl enamels. The coating is quick-drying and has water, oil, petrol and salt resistance, as well as weather resistance.

ADVANTAGES

the possibility of applying a large wet film thickness;
high mechanical stability.

RECOMMENDATIONS TO USE — is used to protect the internal surfaces of pipelines, metal containers, tanks, process equipment, concrete tanks, general-purpose metal structures that require high protection from chemical exposure, as well as at high abrasive and shock loads of the environment.

PRODUCT SPECIFICATIONS

recommended dry / wet thickness 70 / 200µm
drying time (20 ° С): up to degree 3 — 1 h
suitability of the mixture for use at 20 ° С when mixed with hardener No. 1 for at least 120 h, when mixed with PEPA for at least 48 h
time of complete curing of the coating at 20 ° С — 2 days
theoretical consumption for a dry coating 70 µm thick — 280g / m2
dry residue (± 2) — 35-40% of the mass.
recommended number of layers — 2

COATING TYPE — matte

COLORS — green, black, sulfur, light gray, red-brown. Enamel tinting is possible according to the RAL catalog.

COATING AND APPLICATION COATING

Enamel Farbacoat EP-152 comes in two containers. To prepare the base of enamel, you must first mix well and add to 100 cc. — 1.1 cc hardener No. 1 or 0.55 in.h. PEPA, mix again and incubate for 30 minutes. If necessary, after the introduction of the hardener, the enamel can be diluted to a working viscosity with a solvent R-5A or R-5 in an amount of not more than 50% by weight of the enamel.

The suitability of the mixture is 120 hours with hardener No. 1 and 48 hours with hardener PEP at a temperature of 20 ° C. Higher temperatures shorten the life of the mixture, lower temperatures prolong it.

After mixing the components, the product must be used within the indicated pot life.

Method of applying the finished enamel:

airless spraying: ∅ 0,28-0,43mm; 10-15 MPa;
brush;
roller;
air spraying ∅ 1.7-2.0 mm (after dilution to a viscosity of 14-20 s according to B3-246 viscometer. Nozzle ø4 mm).

MODE OF APPLICATION

The better prepared the surface, the more resistant the coating will be. Coatings applied directly to steel surfaces that have undergone abrasive blasting to a minimum degree of cleaning Sa 2½ according to ISO 8501 or 2 according to GOST 9.402 have the best chemical and mechanical resistance. The surface prepared for coating should be dry, free from salt, grease, dust and other contaminants.

To avoid moisture condensation, the surface temperature should be above the dew point temperature by at least 3 ° C. drying time of a single-layer coating at a temperature of (20 ± 2) ° С — not more than 60 minutes. At a lower temperature or relative humidity of more than 65%, the drying time can be increased. After drying one layer, subsequent layers are applied in the same way, with a minimum overlap interval of one hour.