Primer Farbacoat EP-045

The primer Farbacoat EP-045 has high anticorrosive and physicomechanical properties, can be operated in a temperate, cold and tropical climate.

Two-component epoxy primer Farbacoat EP-045 has high anti-corrosion and physical properties. Designed for use in different climatic zones.

ADVANTAGES

the possibility of applying a large wet film thickness;
high mechanical stability;
very high adhesion to steel, galvanized and aluminum surfaces.

RECOMMENDATIONS FOR USE

The Fabracoat EP-045 primer is designed for high-quality anticorrosive protection of metal products (carbon and galvanized steel, copper, aluminum and its alloys), in machine building, machine building, car building and shipbuilding, in construction and other industries, as well as during repair works

SPECIFICATIONS

recommended dry / wet thickness is 50/120 microns;
drying time (20 ° С): up to degree 3 — 6 h;
suitability of the mixture for use at 20 ° С for at least 8 h;
theoretical consumption for a dry coating 60µm thick — 180g / m2
dry residue (± 2) — 65% by weight;
The recommended number of layers is 1-2.

COATING TYPE — matte

COLOR — brown beige

COATING AND APPLICATION COATING

Primer Farbacoat EP-045 is supplied in the form of two components: a prefabricated primer and an F-45 hardener.

Components must be mixed immediately before use, 14 parts by weight of F-45 hardener is added to 100 parts by weight of the semi-finished primer. The primer is kept for 15-30 minutes. and diluted to working viscosity with solvent Р-5А or Р-5. The viability of the finished primer is not less than 8 hours at a temperature of (20 ± 2) ° C.

APPLICATION METHOD

airless spraying: ø nozzle 0,28-0,43mm; pressure of 10-15 MPa;
brush;
roller;
air spraying ø nozzle 1.9-2.5 mm (after dilution to viscosity 15s according to viscometer B3-246, nozzle ø 4 mm).

MODE OF APPLICATION

The better the surface is prepared, the more resistant the coating will be. Coatings applied directly to steel surfaces that have undergone abrasive blasting to a minimum degree of cleaning Sa 2½ according to ISO 8501 or 2 according to GOST 9.402 have the best chemical and mechanical stability. The surface prepared for coating should be dry, free from salt, grease, dust and other contaminants. To avoid moisture condensation, the surface temperature should be above the dew point temperature by at least 3 ° C. The drying time of a single-layer coating at a temperature of (20 ± 2) ° C is 6 hours. At a lower temperature or relative humidity of more than 65%, the drying time can be increased. After drying one layer, the subsequent layers are applied similarly, with a minimum overlap interval of 1 hour.

WARRANTY PERIOD OF STORAGE

Store in closed original packaging at a temperature from +5 to + 35 ° С

component I — 6 months from the date of manufacture

component II — 6 months